| Property | Value | Method |
|---|---|---|
| Tensile Properties | ||
| Young’s Modulus | 2.6 +/- 0.1 GPa | ASTM D638 |
| Ultimate Tensile Strength | 70 +/- 1 MPa | ASTM D638 |
| Elongation at Break | > 7% | ASTM D638 |
| Tensile Toughness | > 10 MPa | ASTM D638 |
| Flexural Properties | ||
| Flexural Modulus | 1.9 +/- 0.1 GPa | ASTM D790 |
| Ultimate Flexural Strength | 51 +/- 1 MPa | ASTM D790 |
| Thermal Properties | ||
| Glass Transition Temperature (Tg) | ||
| Tg by DSC | 151 +/- 1 °C | ASTM E1356 |
| Tg by Peak of Loss Modulus Curve at 1 Hz | 150 °C | D4065 |
| Heat Deflection Temperature (HDT) | ||
| HDT Method A: 0.455 MPa | 138 °C | ASTM E2092 |
| HDT Method B: 1.82 MPa | 129 °C | ASTM E2092 |
| Impact Strength | ||
| Un-notched IZOD | > 800 J/m | |
| Notched IZOD | 34 +/- 2 J/m | ASTM D256 |
| Hardness | ||
| Shore D Hardness | 84 +/- 1 D | D2240 |